光强度对双固化树脂黏接剂与牙本质黏接强度的影响

摘要
图/表
参考文献
相关文章 (3)

全文: PDF (500 KB) RICH HTML
输出: BibTeX | EndNote (RIS)

摘要目的比较不同光强度对双固化树脂黏接剂与牙本质的黏接强度影响。方法将40颗恒磨牙，暴露咬合面牙本质后随机分为两组，每组20颗牙。DC组用双重固化树脂黏接剂Clearfil DC Bond处理，SE组用光固化树脂黏接剂Clearfil SE Bond处理后，端端对接从近中方向光照。将黏接试样沿光照方向切成5片(1 mm/片，L_1~5)，再将每片垂直黏接界面切出5个微拉伸样本(1 mm×1 mm)，测试两组黏接强度(mTBS)。结果随着穿透牙本质厚度增加，光强度降低导致黏接强度下降。部分样本在制备时发生界面折断，SE组存留样本L₁ 70%，L₂ 30%，L_3~5为0;DC组L_1~5分别为68%，86%，56%，44%和38%。SE 组L_1~5黏接强度分别为:(13.22±8.64)MPa，(7.49±3.88)MPa，0、0、0 MPa;DC组为:(11.25±4.11)MPa，(9.69±5.07) MPa，(8.13±4.88)MPa，(6.83±3.53)MPa和(5.56±2.95) MPa。两组表面两层黏接强度无统计学差异。结论双固化黏接剂与牙本质的黏接强度随着固化光穿透牙本质深度的增加而降低。

	服务

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章

关键词 ：光强度, 双固化, 黏接剂, 黏接强度

Abstract：Objective To evaluate the intensity of irradiation after penetrating dentin, and compare the effects of cure-light on the micro-tensile bond strength (mTBS) of dual-cure dental adhesive.Methods The superficial dentin of occlusal surface (40 molars) were exposed and applied with Clearfil DC Bond(A ) or Clearfil SE Bond (B), then bonded together through light-cure from mesial dejection. The bond specimens were cut into sticks(bonding area 1 mm×1 mm) along the direction of light-cure (L_1-5) , and tested with Micro-Tensile Tester for mTBS. The statistical analysis was performed using SPSS11.0.Results After penetrating dentin of 1 mm and 2 mm thickness, the light irradiation decreased to (114±28) mWcm^-2 and (28±11)mWcm^-2, respectively. Some stick samples were broken during preparation, and the fracture occurred at the bonding interface. The remaining samples were SE: L₁ 70%, L₂ 30%, L₃-L₅ 0%; DC: L₁ to L₅ was 68%, 86%, 56%, 44%,38% . The mTBS were (13.22±8.64) MPa (L₁), (7.49±3.88) MPa (L₂) and 0 MPa (L₃ and L₄) for SE,(11.25±4.11) MPa (L₁), (9.69±5.07) MPa (L₂), (8.13±4.88) MPa (L₃), (6.83±3.53) MPa (L₄) and (5.56±2.95) MPa for DC. There was no significant difference between DC and SE regarding the mTBS of L₁ and L₂.Conclusions The mTBS of dual-cureresin adhesive decreased with the increase of cure-light penetrating depth of dentin.

Key words： irradiation intensity dual-cure resin adhesive bond strength

收稿日期: 2016-02-15

ZTFLH:

R783.1

作者简介: 祖斌，本科学历，主治医师。

引用本文:

祖斌，苗莉. 光强度对双固化树脂黏接剂与牙本质黏接强度的影响[J]. 武警医学, 2016, 27(6): 574-576. ZU Bin and MIAO Li. Effects of irradiation intensity on the bond strength of dual-cure resin adhesive. Med. J. Chin. Peop. Armed Poli. Forc., 2016, 27(6): 574-576.

链接本文:

http://journal08.magtechjournal.com/Jwk_wjyx/CN/ 或 http://journal08.magtechjournal.com/Jwk_wjyx/CN/Y2016/V27/I6/574

[1]	赵佳萌,王焱,曾晨光,等. 光照模式对双固化树脂粘接剂聚合程度的影响[J].中华口腔医学研究杂志(电子版),2013,7(5):357-361.
[2]	Papazoglou E, Rahiotis C, Kakaboura A, et al. Polymerization efficiency of dual-polymerized resin cements light-irradiated through ceramics andlaboratory-processed resin composite[J]. Eur J Prosthodont Restor Dent,2008,16(1):15-19.
[3]	Feng L, Carvalho R, Suh B I. Insufficient cure under the condition of highirradiance and short irradiation time[J]. Dent Mater, 2009,25(3):283-289.
[4]	Breschi L, Mazzoni A, Ruggeri A, et al. Dental adhesion review: agingand stability of the bonded interface[J]. Dent Mater, 2008,24(1):90-101.
[5]	Jung H, Friedl K H, Hiller K A, et al. Curing efficiency of differentpolymerization methods through ceramic restorations[J]. Clin OralInvestig, 2001,5(3):156-161.
[6]	Aravamudhana K, Rakowskib D, Fanc P L. Variation of depth of cure and intensity withdistance using LED curing lights [J]. Dent mater, 2006,22(11):988-994.
[7]	Felix C A,Price R B.The effect of distance from light source on light intensity from curing lights[J].J Adhes Dent,2003,5(4):283-291.
[8]	Rode K M,Kawano Y,Turbino M L.Evaluation of curing light distance on resin composite microhardness and polymerization[J].Oper Dent,2007,32(6):571-578.
[9]	Price R B, Murphy D G, Dérand T. Light energy transmissionthrough cured resin composite and human dentin [J].Quintessence Int,2000, 31(9):659-667.
[10]	Ruyter I E, Oysaed H. Conversion in different depths ofultraviolet and visible light activated composite materials [J].Acta Odontol Scand, 1982, 40(3):179-192.
[11]	Ferracane J L, Mitchem J C, Condon J R, et al. Wear and marginal breakdown of composites with various degrees of cure [J].J Dent Res,1997,76(8):1508-1516.
[12]	Sideridou I D, Achilias D S. Elution study of unreactedBis-GMA, TEGDMA, UDMA, and Bis-EMA from light-cureddental resins and resin composites using HPLC [J]. J BiomedMater Res B Appl Biomater, 2005, 74(2):617-626.
[13]	Leprince J G,Palin W M,Hadis M A,et al.Progress in dime thacrylate-based dental composite technology and curing efficiency[J].Dent Mater,2013,29(2):139-156.
[14]	Jung H,Friedl K H, Hiller K A, et al.Polymerization efficiencyof different photocuring units through ceramic discs [J]. Oper Dent, 2006, 31(1):68-77.
[15]	Kilinc E, Antonson S A,Hardigan P C, et al.The effect of ceramic restoration shade and thickness on the polymerization of light- and dual-cure resin cements[J]. Oper Dent, 2011, 36(6): 661-669.
[16]	Pires-de-Souza Fde C, Drubi Filho B, Casemiro L A, et al. Polymerization shrinkage stress of composites photo-activated by different light sources[J]. Braz Dent J, 2009,20(4): 319-324.
[17]	Yoshida K,Atsuta M.Post-irradiation hardening of dual-cured and light-cured resin cements through machinable ceramics[J].Am J Dent,2006,19(5):303-307.
[18]	Lee J W,Cha H S,Lee J H.Curing efficiency of various resin-based materials polymerized through different ceramic thicknesses and curing time [J] .J Adv Prosthodont,2011,3(3):126-131.